CAS No.: 25608-12-2
Other Names: SMC Fiberglass Resin
MF: C3H5NO)n
EINECS No.: 208-750-2
Type: Synthetic Resin And Plastics
Brand Name: Fullmark
Model Number: TC-9510, TC-9510
Appearance: transparent light yellow liquid
Packaging: metal barrel
Usage: SMC Fiberglass Resin
Net Weight: 220kg
Certificate: Msds
Storage Period: 90 days .but it's 30 days if add thixotropice accelerator
Storage Condition: Below 25℃ in dark
Keywords: SMC Fiberglass Resin
Place Of Origin: Jiangsu, China
Purity: 61-67%
Brand: Fullmark
| Selling Units | : | ton |
| Package Type | : | metal barrel |
The file is encrypted. Please fill in the following information to continue accessing it
Ø High reactivity
Ø Good mechanical property
Ø Heat resistance
Ø Stable thickening property
Ø Add with FL series low shrinkage agent and Low profile additive
Ø Finished product low shrinkage , zero shrinkage performance reached to A level surface
Ø Specially for SMC/BMC process
Ø Widely used in automobile, electrical and construction field
SMC Fiberglass Resin property
| Appearance | transparent light yellow liquid | Unit | Testing method |
| Acid value | 11-19 | mgKOH/g | GB/T 2895-2008 |
| Solid content | 57-63 | % | GB/T 7193-2008 |
| Viscosity 25℃ | 0.52-0.87 | Pa.s | GB/T 7193-2008 |
| Stability 80℃ | ≥24 | h | GB/T 7193-2008 |
SMC/sheet moulding compound resin typical curing property
25℃ water bath,100g resin filled with 2ml MEKP solvent and 4ml Cobalt iso-octoate.
gel time 2.9-5.5 min accord to GB/T 7193-2008
80℃ water bath,100g resin filled with 1g BPO powder
gel time 7.9-14.70 min accord to GB/T 7193-2008
65℃-Tmax 8.4-15.6 min
Tmax 215-235 ℃
SMC Fiberglass Resin property
| Item | Unit | Testing method |
| Appearance | Casting body no fault |
|
| Tensile strength | 60 Mpa | GB/T 2567-2008 |
| Tensile modulus | 3700 Mpa | GB/T 2567-2008 |
| Elongation at break | 2% | GB/T 2567-2008 |
| Bending strength | 115 Mpa | GB/T 2567-2008 |
| Bending modulus | 4000 Mpa | GB/T 2567-2008 |
| Impact strength | 13 KJ/m2 | GB/T 2567-2008 |
| Distortion temperature | 120 ℃ | GB/T 1634-2004 |
| Barcol hardness | 45 | GB/T 3854-2005 |
| Line shrinkage | 0.8% | GB/T 15585-1995 |
SMC Fiberglass Resin package and storage conditions
Fiberglass resin packed in metal barrel , 220kg/barrel (about 55 gallons)
Try to prevent fiberglass resin from exposure to sunshine and heat resource
Prohibit opening before use
Fiberglass resin is flammable, should keep away from open fire
Fiberglass shelf life is 3 month under 25℃
Unsaturated Polyester resin features high
production efficiency due to the fact that it cures quickly and has excellent coloring properties. It has outstanding strength, chemical resistance, heat resistance, and electrical properties. Unsaturated Polyester Resin reinforced with Glass Fiber is a typical example of Fiber Reinforced Plastics (FRP).
It has high mechanical strength and is widely used for plastic products requiring high strength for use in applications such as construction materials, bathtubs, boats, ship parts, and helmets.
SMC/sheet moulding compound resin used in manufacturing enclusures , cabinets and boxes , lamps housing low and medium voltage insulators conductive & ATEX
Our Services
contact me for more details of our products
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now